Anycubic ABS-Like Resin 3.0
High-Toughness Resin for Functional Parts & Engineering Prototypes
Anycubic ABS-Like Resin 3.0 is a high-performance photopolymer resin engineered to deliver the durability, toughness, and reliability required for functional 3D printing applications. Designed to simulate the mechanical characteristics of ABS plastic, this advanced resin combines excellent impact resistance with high dimensional accuracy, making it ideal for mechanical components, electronic housings, automotive parts, and engineering prototypes.
Unlike conventional brittle resins, ABS-Like Resin 3.0 offers enhanced resilience and crack resistance, allowing printed parts to withstand drilling, sanding, polishing, and everyday handling without deformation or failure. Its balanced mechanical properties provide an excellent combination of strength, flexibility, and precision for demanding applications.
Key Features
| Feature | Benefit |
|---|---|
| High Toughness & Crack Resistance | Withstands impact, drilling, and post-processing without cracking |
| High Precision & Low Shrinkage | Produces dimensionally accurate parts with excellent detail |
| Fast Printing Performance | Low viscosity promotes rapid resin flow and efficient curing |
| Smooth Surface Finish | Captures intricate details with clean, professional results |
| Minimal Odor Formula | More comfortable printing experience |
| Wide Printer Compatibility | Compatible with most LCD and DLP resin printers using 365–405nm UV light |
Exceptional Mechanical Performance
ABS-Like Resin 3.0 is formulated to provide excellent durability while maintaining enough flexibility to resist sudden impacts and mechanical stress. With elongation at break reaching up to 30%, printed parts can tolerate greater deformation before failure compared to many traditional rigid resins.
Mechanical Properties
| Property | Value |
|---|---|
| Shore Hardness | 83–86 HD |
| Tensile Strength | 38–45 MPa |
| Elongation at Break | 25–30% |
| Izod Impact Strength | 130 J/m |
| Bending Strength | 50–65 MPa |
| Young’s Modulus | 1300–1700 MPa |
| Bending Modulus | 1500–2000 MPa |
These properties make the material suitable for:
- Mechanical assembly components
- Electronic enclosures and chassis
- Automotive interior components
- Functional engineering prototypes
- Durable display models
- Fixtures and jigs
- Product development testing
High Precision & Low Shrinkage
Designed for dimensional accuracy, Anycubic ABS-Like Resin 3.0 features a controlled volume shrinkage rate of only 3.9–4.9%, helping maintain tight tolerances and preserving intricate design details throughout the printing process.
Whether producing detailed miniatures, precision mechanical components, or engineering prototypes, the resin accurately reproduces:
- Fine surface textures
- Sharp edges
- Small features
- Complex geometries
- Smooth surfaces
Physical Properties
| Property | Value |
|---|---|
| Density | 1.06–1.09 g/cm³ |
| Viscosity (25°C) | 280–300 mPa·s |
| Volume Shrinkage Rate | 3.9–4.9% |
| Material Type | Photopolymer Resin |
| UV Wavelength | 365–405 nm |
Faster Printing Through Lower Viscosity
With a viscosity of only 280–300 mPa·s at 25°C, ABS-Like Resin 3.0 flows quickly and evenly across the build surface. This improved fluidity allows the resin to refill exposed areas more rapidly between layers, supporting faster print cycles while maintaining excellent print quality and structural integrity.
The result is:
- Reduced print times
- Improved layer consistency
- Better surface finish
- Reliable curing performance
Recommended Printing Parameters
| Parameter | Recommended Range |
|---|---|
| Print Environment | 20–40°C |
| Print Temperature | 20–50°C |
| Normal Exposure Time | 2–3.6 seconds |
| Bottom Exposure Time | 23–40 seconds |
| Typical Layer Height | 0.05 mm |
| UV Wavelength | 365–405 nm |
Actual exposure settings may vary depending on printer model, screen type, and environmental conditions.
Simple Post-Processing
For optimal results, clean printed parts thoroughly before final curing.
Post-Processing Specifications
| Parameter | Value |
|---|---|
| Cleaning Solution | ≥95% IPA |
| Washing Duration | ≥3 minutes |
| UV Curing Wavelength | 405 nm |
| Curing Temperature | 18–30°C |
| UV Intensity | 25,000–30,000 μW/cm² |
| Recommended Cure Time | 3 minutes |
After proper curing, printed parts exhibit enhanced strength, durability, and dimensional stability.
Wide Compatibility
Anycubic ABS-Like Resin 3.0 is compatible with a broad range of LCD and DLP resin 3D printers utilizing UV light sources within the 365–405nm wavelength range. This ensures seamless integration with most consumer and professional resin printing systems.
Compatible applications include:
- Engineering prototypes
- Functional production parts
- Product development
- Educational projects
- Automotive prototyping
- Consumer product design
- Workshop and laboratory use
Technical Specifications Summary
| Category | Specification |
|---|---|
| Material | Photopolymer Resin |
| Hardness | 83–86 HD |
| Tensile Strength | 38–45 MPa |
| Elongation at Break | 25–30% |
| Izod Impact Strength | 130 J/m |
| Density | 1.06–1.09 g/cm³ |
| Viscosity | 280–300 mPa·s |
| Shrinkage Rate | 3.9–4.9% |
| UV Compatibility | 365–405 nm |
| Normal Exposure | 2–3.6 s |
| Bottom Exposure | 23–40 s |
| Print Environment | 20–40°C |
| Recommended Cleaning | ≥95% IPA |
| Cure Time | 3 minutes |
Build Stronger, More Durable Prints
Combining high toughness, excellent impact resistance, low shrinkage, and exceptional print quality, Anycubic ABS-Like Resin 3.0 is an excellent choice for makers, engineers, and professionals who require durable, functional parts without sacrificing precision or surface quality.